Product Description for Wholesale Price Spray Activator Cyanoacrylate Adhesive Super Glue MDF Kit for Instant Solution
| 1.High bonding strength | This adhesive is specifically formulated to provide strong and durable bonds. It offers excellent adhesion properties, allowing it to create reliable and long-lasting connections between various materials. |
| 2. Effective on uneven substrates | This adhesive is particularly well-suited for bonding difficult substrates that have an uneven or irregular nature. It addresses the challenge of uneven surfaces by preventing the adhesive from being absorbed too quickly, which could weaken the bond. By slowing down absorption, it increases the overall bonding strength and ensures a more secure attachment. |
| 3.Suitable for vertical surfaces: | One notable feature of Shuode high bonding adhesive is its ability to be used on vertical surfaces without dripping or slumping. This characteristic ensures that the adhesive stays in place during application, making it ideal for projects where gravity comes into play. |
| 4. Overall | Higlue high bonding adhesive offers both high bonding strength and versatility in terms of application. It is especially useful for vertical surfaces and challenging substrates, providing reliable adhesion even in demanding situations. |
Product feature for Spray Activator Cyanoacrylate Adhesive Super Glue MDF Kit for Instant Solution.
1.Bonds Within Seconds
2.High Bonding Power
3. Even Suitable On Uneven Surfaces
Product Parameters
| NAME | Super Glue MDF Kit | |
| DENSITY | 1.0+0.1 | g/ml |
| SOLID CONTENT | ≥25±3 | % |
| VISCOSITY | 400±500 | Mpa.s |
| LNITIAL ADHESION SHEAR STRENGTH | ≥20.8 | Mpa |
| LNITIAL ADHESION PEELING STRENGTH | ≥0.7 | KN/m |
| SHEAR STRENGTH (AFTER 48 HOURS) | ≥1.95 | Mpa |
| PEELING STRENGTH (AFTER 48HOURS) | ≥3.3 | KN/m |
| CURING TIME | 24-48 | hours |
| TEMPERATURE RESISTANCE | -40°C~180°C |
Application Areas
It is suitable for the bonding of a very wide range of materials, including acidic surfaces
(thanks to activator) and some porous ones, where rapid bonding times are required.
Suitable for MDF, wood, chip wood, rubber, most plastics, leather and other common
substrates. Especially suitable for the applications where cure speed needs to be
accelerated. Although it has a degree of gap filling ability, it is generally
recommended for use on close-fitting parts and fairly smooth, even surfaces.